Orion Vesta
| Orion Vesta |
| Type |
Indication |
Colour |
| IV |
5,7,9 |
white |
| Au |
Pt |
Pd |
Ag |
Rh |
Ir |
Cu |
Sn |
Zn |
In |
Ga |
Rest |
| 2,0 |
- |
78,9 |
- |
- |
x |
10,0 |
- |
- |
- |
9,0 |
- |
| Melting interval |
Density |
E-Modulus |
| 1170°C to 1190°C |
10,7 g/cm² |
123 GPa |
| Preheat temp. |
Casting temp. elec. |
Crucible |
| 900°C |
1400°C |
ceramic |
|
 |
| Hardness HV5 |
Tensile limit MPa |
| As cast |
310 |
After firing |
310 |
As cast |
980 |
After firing |
880 |
| Hard |
325 |
Soft |
310 |
Hard |
950 |
|
|
| Tensile strength MPa |
Elongation % |
| As cast |
1250 |
After firing |
970 |
As cast |
15 |
After firing |
15 |
| Hard |
1100 |
|
|
Hard |
12 |
|
|
| TEC |
Recommended solders |
| 25 - 500 °C |
13,8 µm/m.K |
Before firing |
Orion 1090°C wit |
| 25 - 600 °C |
14,0 µm/m.K |
After firing |
PP solder 820°C |
| Oxidation (without vacuum) |
Hardening (cooldown by air) |
| 950°C |
5 minutes |
700°C |
15 minutes |
|
|
|