Orion UX Plus
| Orion UX Plus |
| Type |
Indication |
Colour |
| IV |
5,7,9 |
white |
| Au |
Pt |
Pd |
Ag |
Rh |
Ir |
Cu |
Sn |
Zn |
In |
Ga |
Rest |
| 77,1 |
7,7 |
9,5 |
2,0 |
- |
- |
- |
x |
- |
3,5 |
- |
- |
| Melting interval |
Density |
E-Modulus |
| 1150°C to 1235°C |
17,8 g/cm² |
100 GPa |
| Preheat temp. |
Casting temp. elec. |
Crucible |
| 800°C |
1350°C |
graphite/ceramic/glass carbon |
|
 |
| Hardness HV5 |
Tensile limit MPa |
| As cast |
220 |
After firing |
235 |
As cast |
580 |
After firing |
600 |
| Hard |
265 |
Soft |
130 |
Hard |
640 |
|
|
| Tensile strength MPa |
Elongation % |
| As cast |
760 |
After firing |
740 |
As cast |
10 |
After firing |
7 |
| Hard |
770 |
|
|
Hard |
5 |
|
|
| TEC |
Recommended solders |
| 25 - 500 °C |
14,1 µm/m.K |
Before firing |
1090°C wit / 1060°C PdF geel |
| 25 - 600 °C |
14,3 µm/m.K |
After firing |
II PdF 800°C / III PdF 750°C |
| Oxidation (without vacuum) |
Hardening (cooldown by air) |
| 950°C |
5 minutes |
650°C |
15 minutes |
|
|
|