Orion UX
| Orion UX |
| Type |
Indication |
Colour |
| IV |
5,7,9 |
white |
| Au |
Pt |
Pd |
Ag |
Rh |
Ir |
Cu |
Sn |
Zn |
In |
Ga |
Rest |
| 77,0 |
9,6 |
9,2 |
1,5 |
- |
x |
x |
x |
- |
1,5 |
- |
Re,Fe |
| Melting interval |
Density |
E-Modulus |
| 1145°C to 1255°C |
18,0 g/cm² |
92 GPa |
| Preheat temp. |
Casting temp. elec. |
Crucible |
| 850°C |
1400°C |
graphite/ceramic/glass carbon |
|
 |
| Hardness HV5 |
Tensile limit MPa |
| As cast |
200 |
After firing |
225 |
As cast |
530 |
After firing |
520 |
| Hard |
265 |
Soft |
200 |
Hard |
690 |
|
|
| Tensile strength MPa |
Elongation % |
| As cast |
690 |
After firing |
690 |
As cast |
7 |
After firing |
12 |
| Hard |
780 |
|
|
Hard |
8 |
|
|
| TEC |
Recommended solders |
| 25 - 500 °C |
13,8 µm/m.K |
Before firing |
1120°C lichtgeel / 1060°C PdF geel |
| 25 - 600 °C |
14,0 µm/m.K |
After firing |
II PdF 800°C / III PdF 750°C |
| Oxidation (without vacuum) |
Hardening (cooldown by air) |
| 950°C |
5 minutes |
500°C |
15 minutes |
|
|
|