Orion Isis Plus
| Orion Isis Plus |
| Type |
Indication |
Colour |
| IV |
5,7,9 |
white |
| Au |
Pt |
Pd |
Ag |
Rh |
Ir |
Cu |
Sn |
Zn |
In |
Ga |
Rest |
| 15,0 |
0,2 |
52,0 |
22,5 |
- |
- |
- |
6,4 |
1,6 |
2,0 |
- |
Ru |
| Melting interval |
Density |
E-Modulus |
| 1200°C to 1280°C |
12,2 g/cm² |
110 GPa |
| Preheat temp. |
Casting temp. elec. |
Crucible |
| 900°C |
1400°C |
ceramic |
|
 |
| Hardness HV5 |
Tensile limit MPa |
| As cast |
220 |
After firing |
250 |
As cast |
590 |
After firing |
520 |
| Hard |
260 |
Soft |
160 |
Hard |
530 |
|
|
| Tensile strength MPa |
Elongation % |
| As cast |
900 |
After firing |
760 |
As cast |
24 |
After firing |
20 |
| Hard |
780 |
|
|
Hard |
18 |
|
|
| TEC |
Recommended solders |
| 25 - 500 °C |
14,2 µm/m.K |
Before firing |
Orion 1090°C wit |
| 25 - 600 °C |
14,4 µm/m.K |
After firing |
PP solder 820°C |
| Oxidation (without vacuum) |
Hardening (cooldown by air) |
| 950°C |
5 minutes |
700°C |
15 minutes |
|
|
|