Orion GX
| Orion GX |
| Type |
Indication |
Colour |
| IV |
5,7,9 |
light yellow |
| Au |
Pt |
Pd |
Ag |
Rh |
Ir |
Cu |
Sn |
Zn |
In |
Ga |
Rest |
| 84,0 |
8,0 |
5,0 |
0,9 |
- |
x |
x |
x |
- |
1,0 |
- |
Re,Fe |
| Melting interval |
Density |
E-Modulus |
| 1105°C to 1215°C |
18,3 g/cm² |
95 GPa |
| Preheat temp. |
Casting temp. elec. |
Crucible |
| 800°C |
1310°C |
graphite/ceramic/glass carbon |
|
 |
| Hardness HV5 |
Tensile limit MPa |
| As cast |
165 |
After firing |
190 |
As cast |
390 |
After firing |
420 |
| Hard |
240 |
Soft |
160 |
Hard |
640 |
|
|
| Tensile strength MPa |
Elongation % |
| As cast |
560 |
After firing |
600 |
As cast |
15 |
After firing |
13 |
| Hard |
700 |
|
|
Hard |
7 |
|
|
| TEC |
Recommended solders |
| 25 - 500 °C |
14,1 µm/m.K |
Before firing |
Orion solder 1060°C PdF geel |
| 25 - 600 °C |
14,3 µm/m.K |
After firing |
II PdF 800°C / III PdF 750°C |
| Oxidation (without vacuum) |
Hardening (cooldown by air) |
| 950°C |
5 minutes |
500°C |
15 minutes |
|
|
|