Orion Argos
| Orion Argos |
| Type |
Indication |
Colour |
| IV |
5,7,9 |
white |
| Au |
Pt |
Pd |
Ag |
Rh |
Ir |
Cu |
Sn |
Zn |
In |
Ga |
Rest |
| 0,1 |
- |
53,3 |
36,3 |
- |
- |
- |
7,0 |
x |
2,0 |
- |
Ru |
| Melting interval |
Density |
E-Modulus |
| 1200°C to 1275°C |
10,6 g/cm² |
118 GPa |
| Preheat temp. |
Casting temp. elec. |
Crucible |
| 800°C |
1400°C |
ceramic |
|
 |
| Hardness HV5 |
Tensile limit MPa |
| As cast |
255 |
After firing |
245 |
As cast |
630 |
After firing |
540 |
| Hard |
275 |
Soft |
170 |
Hard |
650 |
|
|
| Tensile strength MPa |
Elongation % |
| As cast |
870 |
After firing |
800 |
As cast |
9 |
After firing |
17 |
| Hard |
880 |
|
|
Hard |
10 |
|
|
| TEC |
Recommended solders |
| 25 - 500 °C |
14,7 µm/m.K |
Before firing |
Orion solder 1090°C wit |
| 25 - 600 °C |
15,0 µm/m.K |
After firing |
II PdF 800°C / III PdF 750°C |
| Oxidation (without vacuum) |
Hardening (cooldown by air) |
| 950°C |
5 minutes |
700°C |
15 minutes |
|
|
|