BioGold AN
| BioGold AN |
| Type |
Indication |
Colour |
| IV |
5,7,9 |
rich yellow |
| Au |
Pt |
Pd |
Ag |
Rh |
Ir |
Cu |
Sn |
Zn |
In |
Ga |
Rest |
| 86,0 |
11,0 |
- |
- |
x |
x |
- |
- |
1,5 |
x |
- |
Nb,Fe |
| Melting interval |
Density |
E-Modulus |
| 1040°C to 1140°C |
18,7 g/cm² |
93 GPa |
| Preheat temp. |
Casting temp. elec. |
Crucible |
| 800°C |
1235°C |
graphite/ceramic/glass carbon |
|
 |
| Hardness HV5 |
Tensile limit MPa |
| As cast |
175 |
After firing |
200 |
As cast |
455 |
After firing |
500 |
| Hard |
210 |
Soft |
140 |
Hard |
580 |
|
|
| Tensile strength MPa |
Elongation % |
| As cast |
575 |
After firing |
600 |
As cast |
8 |
After firing |
8 |
| Hard |
650 |
|
|
Hard |
4 |
|
|
| TEC |
Recommended solders |
| 25 - 500 °C |
14,3 µm/m.K |
Before firing |
Orion 1030°C PdF geel |
| 25 - 600 °C |
14,6 µm/m.K |
After firing |
II PdF 800°C / III PdF 750°C |
| Oxidation (without vacuum) |
Hardening (cooldown by air) |
| 950°C |
3 minutes |
500°C |
15 minutes |
|
|
|