Welcome to Elephant Dental
| Carrara Original System |
|
Au |
Pt |
Pd |
Ag |
Wax table |
Solder |
| Carrara PdF |
75,0 |
9,0 |
- |
12,5 |
convert |
pre |
post |
| Cera H |
73,1 |
1,5 |
5,8 |
16,0 |
convert |
pre |
post |
| Cera R Plus |
58,0 |
20,0 |
8,0 |
27,9 |
convert |
pre |
post |
| Cera Star |
42,0 |
-
|
15,0 |
32,9 |
convert |
pre |
post |
| [ more carrara original system alloys ] |
| Gold ceramic alloys |
|
Au |
Pt |
Pd |
Ag |
Wax table |
Solder |
| BioGold Pure |
99,8 |
- |
- |
x |
convert |
|
|
| BioGold Plus |
86,5 |
10,5 |
- |
- |
convert |
pre |
post |
| Bermudent Y |
86,0 |
11,0 |
- |
- |
convert |
pre |
post |
| Orion UX Plus |
77,1 |
7,7 |
9,5 |
2,0 |
convert |
pre |
post |
| [ more gold ceramic alloys ] |
| Gold-palladium ceramic alloys |
|
Au |
Pt |
Pd |
Ag |
Wax table |
Solder |
| Orion Vesta |
2,0 |
- |
78,9 |
-
|
convert |
pre |
post |
| Orion Isis Plus |
15,0 |
0,2 |
52,0 |
22,5 |
convert |
pre |
post |
| Palladium-silver ceramic alloys |
|
Au |
Pt |
Pd |
Ag |
Wax table |
Solder |
| Orion Argos |
0,1 |
- |
53,8 |
36,3 |
convert |
pre |
post |
| Gold-platinum casting alloys |
|
Au |
Pt |
Pd |
Ag |
Wax table |
Solder |
| Apollo 3 |
74,0 |
1,5 |
1,2 |
13,7 |
convert |
I / II |
| Apollo 3 PdF |
73,0 |
2,0 |
- |
18,5 |
convert |
I / II |
| Apollo 4 PdF |
71,0 |
4,0 |
- |
14,0 |
convert |
I / II |
| Apollo 4 |
70,0 |
4,5 |
2,0 |
13,4 |
convert |
I / II / III |
| [ more gold-platinum casting alloys ] |
| Casting alloys with reduced gold content |
|
Au |
Pt |
Pd |
Ag |
Wax table |
Solder |
| Pluto 4 |
66,5 |
- |
3,5 |
16,7 |
convert |
I / II |
| Pluto 3 |
66,0 |
- |
4,0 |
19,9 |
convert |
I / II / III |
| Minerva 4 PdF |
60,0 |
4,5 |
- |
25,5 |
convert |
I / II |
| Minerva 58 |
58,0 |
1,0 |
3,5 |
24,4 |
convert |
I / II |
| [ more casting alloys with reduced gold content ] |
| Gold-palladium-silver casting alloys |
|
Au |
Pt |
Pd |
Ag |
Wax table |
Solder |
| Pallium 3 |
2,0 |
-
|
26,7 |
60,7 |
convert |
I / II |
| Pallacon |
- |
-
|
25,0 |
70,0 |
convert |
I / II / III |
| Pallium 3 C |
10,0 |
-
|
20,0 |
59,9 |
convert |
I / II / III |
|
|
|